Examination of Oxide Scales Formed During Hot Rolling of Steels
-
T. Höfler
Abstract
Preparation of oxidized steel samples demands special attention, due to the heterogeneous composition combining hard and brittle with soft and ductile phases. Samples of various steels taken from the hot rolling process at voestalpine Stahl GmbH as well as samples oxidized in a horizontal tube furnace under controlled atmosphere are examined. Suitable mounting techniques, including the use of taper section angles to achieve increased depth resolution, and preparation parameters for reproducible and satisfactory results are presented, backed by images taken during various stages of grinding and polishing.
Kurzfassung
Aufgrund der heterogenen Zusammensetzung aus harten, spröden und weichen, duktilen Phasen erfordert die Präparation oxidierter Stahlproben besondere Aufmerksamkeit. Es werden Proben verschiedener Stähle untersucht, die während des Warmwalzens bei voestapline Stahl GmbH entnommen wurden sowie Proben, die unter kontrollierter Atmosphäre in einem horizontalen Rohrofen oxidiert wurden. Es werden Einbettungstechniken, darunter die Nutzung von Winkeln für Schrägschliffe zum Erreichen einer höheren Tiefenauflösung und Präparationsparameter für reproduzierbare und zufriedenstellende Ergebnisse präsentiert, die durch Aufnahmen gestützt werden, die während der diversen Phasen des Schleifens und Polierens gemacht wurden.
References / Literatur
[1] Ginzburg, V. B.; Ballas, R.: Flat Rolling Fundamentals, Marcel Dekker, New York, USA, 2000, p. 36510.1201/9781482277357Suche in Google Scholar
[2] Takeda, M. et al.: Materials Transactions50 (2009) 9, p. 2242–224610.2320/matertrans.M2009097Suche in Google Scholar
[3] Fukagawa, T. et al.: ISIJ International34 (1994) 11, p. 906–91110.2355/isijinternational.34.906Suche in Google Scholar
[4] Melfo, W. et al.: ISIJ International53 (2013) 5, p. 866–87310.2355/isijinternational.53.866Suche in Google Scholar
[5] Chen, R. Y.; Yuen, W. Y. D.: ISIJ International45 (2005) 1, p. 52–5910.2355/isijinternational.45.1Suche in Google Scholar
© 2019, Carl Hanser Verlag, München
Artikel in diesem Heft
- Contents/Inhalt
- Contents
- Editorial
- Editorial
- Technical Contributions/Fachbeiträge
- Combination of Nanoindentation and Microscopy for the Examination of Aluminum Alloys in Coarse- and Ultrafine-Grained Condition
- Metallographic Contrasting of Weld Joints on Duplex Stainless Steel
- Examination of Oxide Scales Formed During Hot Rolling of Steels
- High Temperature Corrosion of Steel X15CrNiSi25-21 (1.4841) in a Mixed Gas Atmosphere – Sample Preparation and Damage Mechanism
- Meeting Diary/Veranstaltungskalender
- Meeting Diary
Artikel in diesem Heft
- Contents/Inhalt
- Contents
- Editorial
- Editorial
- Technical Contributions/Fachbeiträge
- Combination of Nanoindentation and Microscopy for the Examination of Aluminum Alloys in Coarse- and Ultrafine-Grained Condition
- Metallographic Contrasting of Weld Joints on Duplex Stainless Steel
- Examination of Oxide Scales Formed During Hot Rolling of Steels
- High Temperature Corrosion of Steel X15CrNiSi25-21 (1.4841) in a Mixed Gas Atmosphere – Sample Preparation and Damage Mechanism
- Meeting Diary/Veranstaltungskalender
- Meeting Diary