Pitting Corrosion on a Water Pipe of the Grade 1.4301
-
S. Strobl
Abstract
Pipes made of stainless steel in the drinking water supply system showed pitting corrosion in the heat-affected zone (HAZ) of the welded joints. This was very surprising considering the chemical composition of the fresh water and the fact that no microbiologically influenced corrosion (MIC) had been found.
Testing for pitting corrosion showed no increased sensitivity of the HAZ. The Electrochemical Potentiodynamic Reactivation test (EPR test), however, was positive for the tube interior and only within the HAZ. Metallographic examinations were carried out to clarify if sensitization or intergranular attack, a type of corrosion, were the cause.
The holes showed an irregular propagation which can be explained by segregation lines in the steel. It is noticeable that the holes preferably propagate in the mid-thickness region of the steel sheet. The metallographic samples showed no preferred corrosive attack along the grain boundaries (intergranular attack) and also no sensitization of the steel.
Kurzfassung
Rohrleitungen aus rostfreiem Stahl einer Trinkwasserversorgung zeigten in der Wärmeeinflusszone (WEZ) der Schweißnähte Lochkorrosion. Aufgrund der chemischen Zusammensetzung des Frischwassers und der Tatsache, dass keine mikrobiell induzierte Korrosion (MIK) gefunden wurde, war dies sehr überraschend.
Die Prüfung auf Lochkorrosion zeigte keine erhöhte Empfindlichkeit der WEZ. Die elektrochemische Prüfung auf Sensibilisierung (EPR) ergab jedoch ein positives Ergebnis an der Rohrinnenseite und nur in der WEZ. Metallographische Untersuchungen sollten klären, ob Sensibilisierung oder die Korrosionsform Kornzerfall vorliegt.
Die Löcher zeigen eine unregelmäßige Ausbreitung, welche durch Seigerungszeilen im Stahl erklärt werden kann. Auffällig ist, dass die Löcher sich bevorzugt in der Blechmitte ausbreiten. An den metallographischen Schliffen wurde kein bevorzugter korrosiver Angriff an den Korngrenzen (Kornzerfall) und auch keine Sensibilisierung des Stahls festgestellt.
References / Literatur
[1] Linhardt, P.: Electrochimica Acta51 (27) (2006) 6081–608410.1016/j.electacta.2005.12.056Suche in Google Scholar
[2] Linhardt, P.: Materials and Corrosion61 (12) (2010) 1034–1039. 10.1002/maco.201005769Suche in Google Scholar
[3] Vander Voort, G. F.: Metallography. ASM International, 3rd printing, 2004.10.31399/asm.hb.v09.a0003752Suche in Google Scholar
[4] Strobl, S.; Haubner, R., Linhardt, P.: Praktische Metallographie – Practical Metallography, 49 (2012), 3; 155–170.10.3139/147.110146Suche in Google Scholar
© 2018, Carl Hanser Verlag, München
Artikel in diesem Heft
- Contents/Inhalt
- Contents
- Editorial
- Editorial
- Technical Contributions/Fachbeiträge
- 3D Structural Analysis of Selected High-Temperature Materials
- Morphological Optimization of Graphite in Spheroidal Cast Iron with a Modulus of 4 cm used in the Manufacture of Wind Turbine Hubs
- Pitting Corrosion on a Water Pipe of the Grade 1.4301
- Meeting Diary/Veranstaltungskalender
- Meeting Diary
Artikel in diesem Heft
- Contents/Inhalt
- Contents
- Editorial
- Editorial
- Technical Contributions/Fachbeiträge
- 3D Structural Analysis of Selected High-Temperature Materials
- Morphological Optimization of Graphite in Spheroidal Cast Iron with a Modulus of 4 cm used in the Manufacture of Wind Turbine Hubs
- Pitting Corrosion on a Water Pipe of the Grade 1.4301
- Meeting Diary/Veranstaltungskalender
- Meeting Diary