The Copper of the Kyffhäuser Monument
-
A. Undisz
Abstract
The connection between copper and art goes way back. For thousands of years, the ductile metal has been worked in cold state via hammer and punch to make jewelry, vessels or monuments. More recent examples are the Statue of Liberty in New York, the Quadriga in Berlin and the equestrian statue of Emperor William I at the Kyffhäuser. During the recently completed renovation of the Kyffhäuser monument it was possible to perform a scientific examination on the copper of the equestrian statue. The examinations showed that the material is multiphase due to the content of oxygen and lead. With regard to the mechanical properties, the impurity phases are only of little importance. Details of the microstructure with a spatially coherent order of impurity phases, however, have never been observed in this way. The formation of the microstructure is discussed taking into account the particular circumstances of the artistic shaping via repoussé and chasing.
Kurzfassung
Die Verbindung von Kupfer und Kunst geht weit zurück. Seit Jahrtausenden wird das duktile Metall im kalten Zustand durch Treiben mit Hammer und Punzen zu Schmuck, Gefäßen oder Denkmälern verarbeitet. Jüngere Beispiele sind die Freiheitsstatue in New York, die Quadriga in Berlin und das Reiterstandbild Kaiser Wilhelms I. am Kyffhäuser. Im Zuge der kürzlich abgeschlossenen Sanierung des Kyffhäuserdenkmals konnte eine wissenschaftliche Untersuchung am Kupfer des Reiterstandbildes durchgeführt werden. Die Untersuchungen ergaben, dass der Werkstoff aufgrund des Gehalts an Sauerstoff und Blei mehrphasig ist. Im Hinblick auf die mechanischen Eigenschaften ist den Fremdphasen nur geringe Bedeutung beizumessen. Details des Gefüges mit räumlich zusammenhängender Anordnung der Fremdphasen wurden jedoch in dieser Art bisher nicht beobachtet. Die Entstehung des Gefüges wird unter Einbeziehung der besonderen Gegebenheiten der künstlerischen Formgebung durch das Treiben diskutiert.
References / Literatur
[1] Kühn, A.; KühnH.: Treiben von Kupfer und Kupferlegierungen. Berlin: Deutsches Kupfer-Institut e.V.; (1993)Suche in Google Scholar
[2] Mansfeld – Die Geschichte des Berg- und Hüttenwesens. Lutherstadt Eisleben und Bochum: Verein Mansfelder Berg- und Hüttenleute e.V und Deutsches Bergbau-Museum Bochum; (1999)Suche in Google Scholar
[3] Dies, K.: Kupfer und Kupferlegierungen in der Technik. Berlin/Heidelberg/New York: Springer-Verlag; (1967) 10.1007/978-3-642-48931-0Suche in Google Scholar
[4] Undisz, A.; Freiberg, K. E.; Seide, A.; Koenen, T.; Rettenmayr, M.: Microstructure Preparation Using Glow Discharge Plasma Taking the Examples of Ni-Ti, Cu-Zn and a Ni-Based Alloy. Praktische Metallographie-Practical Metallography53 (2016), 53:86–9710.3139/147.110376Suche in Google Scholar
[5] ASM Specialty Handbook: Copper and Copper Alloys. Materials Park, OH: ASM International; (2001)Suche in Google Scholar
[6] Schumann, H.: Metallographie. Leipzig: VEB Deutscher Verlag für Grundstoffindustrie; (1991)Suche in Google Scholar
[7] ASM Handbook: Metallography and Microstructures. Materials Park, OH: ASM International; (2004)Suche in Google Scholar
[8] Kauczor, E.: Angewandte Metallographie. Berlin / Heidelberg: Springer; (1962) 10.1007/978-3-642-85601-3Suche in Google Scholar
[9] Ecke, B. K.: (05.02.2017); Available from: http://www.harz-saale.de/wordpress/uber-das-kupfererz-oder-kupferschiefer-im-mansfelder-revier-und-seine-nutzung/Suche in Google Scholar
[10] Hinzmann, R.: Nichteisenmetalle: Erster Teil, Kupfer, Messing, Bronze, Rotguss. Berlin: Springer Book Archives; (2013)Suche in Google Scholar
[11] Vagnard, G.; Washburn, J.: Plastic Deformation of Cuprous Oxide. Journal of the American Ceramic Society (1968), 51:8810.1111/j.1151-2916.1968.tb11843.xSuche in Google Scholar
[12] Cancarevic, M.; Zinkevich, M.; Aldinger, F.: Thermodynamic assessment of the ternary Cu-Pb-O system. Zeitschrift Fur Metallkunde96 (2005), 879–8710.3139/146.101126Suche in Google Scholar
© 2017, Carl Hanser Verlag, München
Artikel in diesem Heft
- Contents/Inhalt
- Contents
- Editorial
- Editorial
- Technical Contributions/Fachbeiträge
- The Copper of the Kyffhäuser Monument
- Preparing Soft Magnetic Composites for Structural and Micromechanical Investigations
- Round Robin Test on the “Analysis of Graphite Shapes by Means of Microscopic Images of Cast Iron Samples” in the DGM Working Group “Quantitative Structural Analysis” of the Expert Committee Materialography
- Failure Analysis
- Cracks in Hot-Dip Galvanized Steel Components
- Meeting Diary/Veranstaltungskalender
- Meeting Diary
Artikel in diesem Heft
- Contents/Inhalt
- Contents
- Editorial
- Editorial
- Technical Contributions/Fachbeiträge
- The Copper of the Kyffhäuser Monument
- Preparing Soft Magnetic Composites for Structural and Micromechanical Investigations
- Round Robin Test on the “Analysis of Graphite Shapes by Means of Microscopic Images of Cast Iron Samples” in the DGM Working Group “Quantitative Structural Analysis” of the Expert Committee Materialography
- Failure Analysis
- Cracks in Hot-Dip Galvanized Steel Components
- Meeting Diary/Veranstaltungskalender
- Meeting Diary