Metallurgical Failure Investigation of a Surface Hardened Drive Shaft Made of Tempered Low-Alloy Steel 25CrMo4 (1.7218)

Dedicated to the Lette Verein Berlin on the occasion of its 150th jubilee
  • B. Fischer und E. Cagliyan
Veröffentlicht/Copyright: 25. August 2016
Veröffentlichen auch Sie bei De Gruyter Brill
Manuskript einreichen Informationen für Autor*innen
Practical Metallography
Aus der Zeitschrift Practical Metallography Band 53 Heft 9

Abstract

A drive shaft of a multifunctional mechanical processing machine for large components broke down during processing. The OEM shaft was worn-out after years of operation and was recently replaced. The replaced drive shaft was delivered to the materials laboratory of the Berlin gas turbine plant in order to identify the cause of the damage. It was found that the component failed due to high cycle fatigue failure, HCF, on the tooth roots after a short period of operation. The teeth of the damaged shaft were inappropriately induction surface hardened.

Kurzfassung

Eine Antriebswelle einer multifunktionalen mechanischen Bearbeitungsmaschine für Großkomponenten fiel während des Bearbeitungsvorganges aus. Die Antriebswelle wurde kürzlich ausgetauscht, nachdem die OEM Welle nach mehrjähriger Betriebszeit verschlissen war. Die ausgetauschte Antriebswelle wurde zur Ursachenklärung dem Werkstoffprüflabor des Gasturbinenwerkes Berlin angeliefert. Es wurde festgestellt, dass das Bauteil nach kurzer Betriebsdauer, aufgrund von hochzyklischen Schwingbrüchen (HCF, High Cycle Fatigue Failure) an den Zahnfüßen versagte. Die Zähne der Schadenswelle wurden fehlerhaft induktiv randschichtgehärtet.

Übersetzung: E. Engert

References / Literatur

[1] Interner Bericht LGT QM QL/2014/0192Suche in Google Scholar

[2] DIN EN ISO 18265: 2014-02 Metallische Werkstoffe – Umwertung von HärtewertenSuche in Google Scholar

[3] www.dew-stahl.com/fileadmin/files/dew-stahl.com/documents/Publikationen/Werkstoffdatenblaetter/Baustahl/1.7218_1.7213_de.pdfSuche in Google Scholar

Received: 2016-03-07
Accepted: 2016-03-21
Published Online: 2016-08-25
Published in Print: 2016-09-07

© 2016, Carl Hanser Verlag, München

Artikel in diesem Heft

  1. Contents/Inhalt
  2. Contents
  3. Editorial
  4. Editorial
  5. Technical Contributions/Fachbeiträge
  6. Effect of Preparation on the Correct Interpretation of Thermal Spray Coatings on the Basis of Selected Atmospheric Plasma and Flame Spray Coatings
  7. Microstructural Characterisation of Glass Ceramics as a Component Part of High Pressure Discharge Lamps
  8. Characterization of Ultra Thin Copper Layers
  9. Metallurgical Failure Investigation of a Surface Hardened Drive Shaft Made of Tempered Low-Alloy Steel 25CrMo4 (1.7218)
  10. Meeting Diary/Veranstaltungskalender
  11. Meeting Diary
https://doi.org/10.3139/147.110395

Artikel in diesem Heft

  1. Contents/Inhalt
  2. Contents
  3. Editorial
  4. Editorial
  5. Technical Contributions/Fachbeiträge
  6. Effect of Preparation on the Correct Interpretation of Thermal Spray Coatings on the Basis of Selected Atmospheric Plasma and Flame Spray Coatings
  7. Microstructural Characterisation of Glass Ceramics as a Component Part of High Pressure Discharge Lamps
  8. Characterization of Ultra Thin Copper Layers
  9. Metallurgical Failure Investigation of a Surface Hardened Drive Shaft Made of Tempered Low-Alloy Steel 25CrMo4 (1.7218)
  10. Meeting Diary/Veranstaltungskalender
  11. Meeting Diary
Jetzt anmelden und 20% sparen
Institutioneller Zugang
Wie funktioniert Authentifizierung?
Haben Sie eine Idee, wie wir unsere Website verbessern können?
Bitte schreiben Sie uns.
© 2025 De Gruyter Brill
Heruntergeladen am 9.12.2025 von https://www.degruyterbrill.com/document/doi/10.3139/147.110395/pdf?lang=de
Button zum nach oben scrollen