Defects and Fracture Statistics in Low-Pressure Injection Moulded Alumina Components
-
T. Lube
Abstract
The strength and the defects responsible for failure occurring in tubular alumina components were investigated. Strength testing was performed on machined components in 3-point and 4-point bending. Weibull statistics were applied to describe the strength distributions. Fracture surfaces were investigated using stereo-microscopy and SEM. Fractography revealed that three different types of defects were responsible for failure of the 3-point as well as the 4-point bend specimens. Using an iterative procedure, a separate Weibull distribution for each defect type was evaluated using the data of the two different specimen types.
Kurzfassung
Es wurden die Festigkeit und die Defekte untersucht, die für Schäden verantwortlich sind, die in rohrförmigen Teilen aus Aluminiumoxid auftreten. Die Prüfung der Festigkeit wurde an maschinell bearbeiteten Teilen unter Verwendung von 3-Punkt- und 4-Punktbiegeversuchen durchgeführt. Zur Beschreibung der Festigkeitsverteilungen wurde die Weibull-Statistik angewandt. Die Bruchflächen wurden unter Verwendung von Stereo- und Rasterelektronenmikroskopen untersucht. Durch die Fraktographie wurde offenbar, dass für das Versagen an den Dreipunkt- sowie den Vierpunktbiegeproben drei verschiedene Arten von Defekten verantwortlich waren. Mit Hilfe einer Iterationsmethode wurde eine gesonderte Weibull-Verteilung für jede Art eines Defekts bewertet, wobei die Daten der zwei verschiedenen Probenarten verwendet wurden.
References/Literatur
[1] Danzer, R.; Lube, T.; Supancic, P.; Damani, R.: Advanced Engineering Materials10 (2008), 275–29810.1002/adem.200700347Suche in Google Scholar
[2] Gross, D.; Seelig, T.: Fracture Mechanics, Springer, Berlin, (2006)Suche in Google Scholar
[3] Weibull, W.: A Statistical Theory of the Strength of Materials, Generalstabens Litografiska Anstalts Förlag, Stockholm, (1939)Suche in Google Scholar
[4] Munz, D.; Fett, T.: Ceramics, Springer, Berlin, Heidelberg, (1999)10.1007/978-3-642-58407-7Suche in Google Scholar
[5] Danzer, R.; Supancic, P.; Pascual, J.; Lube, T.: Engineering Fracture Mechanics74 (2007), 2919–293210.1016/j.engfracmech.2006.05.028Suche in Google Scholar
[6] Danzer, R.: Key Engineering Materials223 (2002), 1–1810.4028/www.scientific.net/KEM.223.1Suche in Google Scholar
[7] ASTM C 1684-08 Standard Test Methods for Flexural Strength of Advanced Ceramics at Room Temperature – Cylindrical Rod Strength, (2008)Suche in Google Scholar
[8] Young, W. C.: Roark's Formulas for Stress and Strain, McGraw-Hill, New York, (1989)Suche in Google Scholar
[9] En 843-5: in Advanced Technical Ceramics – Monolithic Ceramics – Mechanical Properties at Room Temperature: Part 5 – Statistical Evaluation, (2007)Suche in Google Scholar
[10] Wachtman, J. B.: Mechanical Properties of Ceramics, Wiley-Interscience, New York, Chichester, (1996)Suche in Google Scholar
© 2011, Carl Hanser Verlag, München
Artikel in diesem Heft
- Contents/Inhalt
- Contents
- Editorial
- Editorial
- Technical Contributions/Fachbeiträge
- The Phase and Microstructural Analysis of Protective Oxide Coatings on Molybdenum
- Defects and Fracture Statistics in Low-Pressure Injection Moulded Alumina Components
- 10.3139/147.110151
- The Metallographer's Role in Damage Analysis
- Meeting Diary/Veranstaltungskalender
- Meeting Diary
Artikel in diesem Heft
- Contents/Inhalt
- Contents
- Editorial
- Editorial
- Technical Contributions/Fachbeiträge
- The Phase and Microstructural Analysis of Protective Oxide Coatings on Molybdenum
- Defects and Fracture Statistics in Low-Pressure Injection Moulded Alumina Components
- 10.3139/147.110151
- The Metallographer's Role in Damage Analysis
- Meeting Diary/Veranstaltungskalender
- Meeting Diary