Mobility of grain boundaries in stress fields

Behaviour of grain boundaries under low cycle deformation
  • Myrjam Winning und Syed Badirujjaman
Veröffentlicht/Copyright: 26. Mai 2013
Veröffentlichen auch Sie bei De Gruyter Brill
Manuskript einreichen Informationen für Autor*innen
Materials Testing
Aus der Zeitschrift Materials Testing Band 46 Heft 3

Abstract

The mobility of grain boundaries under certain conditions is a key factor for the evolution of polycrystalline microstructures and material properties. In recent experiments it was shown that grain boundaries can interact with mechanical stress fields and that the motion of planar grain boundaries, low angle as well as high angle grain boundaries, could be induced by an external mechanical stress field [1,2]. Therefore the current study was performed to investigate the details of grain boundary motion and interactions between definite, planar grain boundaries and the mechanical stress field during high temperature low cycle deformation of high purity aluminium bicrystals. The grain boundary planes were in all cases perpendicular to the loading axis. Experiments were made with large as well as small stresses at different temperatures and numbers of cycles. The displacement of grain boundaries was measured by using optical microscopy, and the microstructural features, as well as orientations of individual grains were recorded by the electron backscatter diffraction technique (EBSD) after each deformation experiment.

Kurzfassung

Die Beweglichkeit von Korngrenzen spielt unter bestimmten Bedingungen eine Schlüsselrolle bei der Entwicklung polykristalliner Gefüge und von Werkstoffeigenschaften. Kürzlich konnte experimentell nachgewiesen werden, dass Korngrenzen mit mechanischen Spannungsfeldern in Wechselwirkung treten können und dass die Bewegung planarer Korngrenzen (Kleinwinkel- sowie Großwinkelkorngrenzen) durch externe mechanische Spannungsfelder ausgelöst werden kann [1,2]. Die vorliegende Studie untersucht die Details der Korngrenzenbewegung sowie die Wechselwirkung zwischen definierten planaren Korngrenzen und dem mechanischen Spannungsfeld während der Low Cycle Verformung bei hohen Temperaturen an hochreinen Aluminium Bikristallen. Die Korngrenzenebenen standen in allen Fällen senkrecht zur Beanspruchungsrichtung. Hierzu wurden Versuche mit hohen und niedrigen Spannungen bei verschiedenen Temperaturen und Beanspruchungs-zyklen durchgeführt. Die Korngrenzenverschiebung wurde mittels lichtmikroskopischer Untersuchungen, die mikrostrukturellen Eigenschaften sowie die individuelle Kornorientierung mittels Electron Backscatter Diffraction (EBSD) nach jedem Verformungsversuch aufgenommen.

Myrjam Winning studied physics at the RWTH Aachen and earned her Ph.D. in physics from the RWTH Aachen in 1999. She is currently group leader of the research group “Crystal Plasticity” at the Institute of Physical Metallurgy and Metal Physcis (RWTH Aachen).

Syed Badirujjaman received his academic education at IIT Kanpur. He is admitted to the doctoral program of the Institute of Physical Metallurgy and Metal Physics (RWTH Aachen) and works in grain boundary mechanics in the research group “Crystal Plasticity”.

References

1 Winning, M.; Gottstein, G.; Shvindlerman, L. S.: Acta Mater. 49 (2001) 21110.1016/S1359-6454(00)00321-9Suche in Google Scholar

2 Winning, M.; Gottstein, G.; Shvindlerman, L. S.: Acta Mater. 50 (2002) 5310.1016/S1359-6454(01)00343-3Suche in Google Scholar

3 Betrabet, H. S.; Raman, V.: Metallurgical Transactions A19 (1988) 1437Suche in Google Scholar

4 Chen, S.; Gottstein, G.: Acta Metall. 36 (1988) 309310.1016/0001-6160(88)90046-6Suche in Google Scholar

5 Langdon, T. G.; Yavari, P.: Acta Metall. 31 (1983) 159510.1016/0001-6160(83)90157-8Suche in Google Scholar

6 Langdon, T. G.; Yavari, P.: Acta Metall. 31 (1983) 160510.1016/0001-6160(83)90158-XSuche in Google Scholar

7 Hu, Y. M.; Wang, Z. G.; Li, G. Y.: Materials Science & Engineering A208 (1996) 260Suche in Google Scholar

8 Weiß, S.; Gottstein, G.: Materials Science & Engineering A256 (1998) 8Suche in Google Scholar

Published Online: 2013-05-26
Published in Print: 2004-03-01

© 2004, Carl Hanser Verlag, München

Artikel in diesem Heft

  1. Inhalt/Contents
  2. Inhalt
  3. Kurzbeiträge
  4. Miniaturisierte Welten in drei Dimensionen
  5. Werkstofftag 2003
  6. Fachbeiträge/Technical Contributions
  7. Mobility of grain boundaries in stress fields
  8. Schweißen artfremder Werkstoffpaarungen
  9. Laserlegieren von Schnellarbeitsstählen
  10. Standardization of the instrumented indentation test
  11. Bohrer für den Nanometerbereich
  12. Spezielle röntgenographische Mikrobeugung
  13. Kurzbeiträge
  14. Mehr Sicherheit im Schienenverkehr
  15. Vorschau/Preview
  16. Vorschau
https://doi.org/10.3139/120.100569

Artikel in diesem Heft

  1. Inhalt/Contents
  2. Inhalt
  3. Kurzbeiträge
  4. Miniaturisierte Welten in drei Dimensionen
  5. Werkstofftag 2003
  6. Fachbeiträge/Technical Contributions
  7. Mobility of grain boundaries in stress fields
  8. Schweißen artfremder Werkstoffpaarungen
  9. Laserlegieren von Schnellarbeitsstählen
  10. Standardization of the instrumented indentation test
  11. Bohrer für den Nanometerbereich
  12. Spezielle röntgenographische Mikrobeugung
  13. Kurzbeiträge
  14. Mehr Sicherheit im Schienenverkehr
  15. Vorschau/Preview
  16. Vorschau
Jetzt anmelden und 20% sparen
Institutioneller Zugang
Wie funktioniert Authentifizierung?
Haben Sie eine Idee, wie wir unsere Website verbessern können?
Bitte schreiben Sie uns.
© 2025 De Gruyter Brill
Heruntergeladen am 25.10.2025 von https://www.degruyterbrill.com/document/doi/10.3139/120.100569/pdf
Button zum nach oben scrollen