The Effects of Different P2O5 Content and Basicity on Phosphorus Enrichment in the CaO-SiO2-FetO-P2O5 Slag System

  • L.H. Zhao EMAIL logo , Y.J. Zhang , H.M. Zhou , P. Xu and Y.P. Bao
Published/Copyright: January 14, 2015
Download Article (PDF)
Become an author with De Gruyter Brill
Submit Manuscript Author Information
High Temperature Materials and Processes
From the journal High Temperature Materials and Processes Volume 34 Issue 7

Received: 2014-5-26
Accepted: 2014-10-2
Published Online: 2015-1-14
Published in Print: 2015-11-1

©2015 by De Gruyter

Articles in the same Issue

  1. Frontmatter
  3. The Influence of the Induced Ferrite and Precipitates of Ti-bearing Steel on the Ductility of Continuous Casting Slab
  4. Study on Evolution of Ti-containing Intermetallic Compounds in Alloy 2618-Ti during Homogenization
  5. The Effects of Different P2O5 Content and Basicity on Phosphorus Enrichment in the CaO-SiO2-FetO-P2O5 Slag System
  6. Dry Sliding Wear Behaviours of Valve Seat Inserts Produced from High Chromium White Iron
  7. A Characterization for the Hot Flow Behaviors of As-extruded 7050 Aluminum Alloy
  8. A Characterization of Hot Flow Behaviors Involving Different Softening Mechanisms by ANN for As-Forged Ti-10V-2Fe-3Al Alloy
  9. Effect of Microwave Heating Conditions on the Preparation of High Surface Area Activated Carbon from Waste Bamboo
  10. Laboratory Study on Oxide Inclusions in High-Strength Low-Alloyed Steel Refined by Slag with Basicity 2–5
  11. Processing and Characterization of CrB2-Based Novel Composites
  12. Dispersion of Particles in the Emulsion by the Electric Current
  13. Description of Grain Refinement by Dynamic Recrystallization Under Hot Compressions for As-Extruded 3Cr20Ni10W2 Heat-Resistant Alloy
  14. Identification of Stable Processing Parameters in Ti–6Al–4V Alloy from a Wide Temperature Range Across β Transus and a Large Strain Rate Range
  15. Life Estimation and Creep Damage Quantification of Service Exposed Reformer Tube
https://doi.org/10.1515/htmp-2014-0089
Keywords for this article
phosphorus-enrichment; phosphorus distribution; phosphorus capacity
Creative Commons
BY-NC-ND 3.0

Articles in the same Issue

  1. Frontmatter
  3. The Influence of the Induced Ferrite and Precipitates of Ti-bearing Steel on the Ductility of Continuous Casting Slab
  4. Study on Evolution of Ti-containing Intermetallic Compounds in Alloy 2618-Ti during Homogenization
  5. The Effects of Different P2O5 Content and Basicity on Phosphorus Enrichment in the CaO-SiO2-FetO-P2O5 Slag System
  6. Dry Sliding Wear Behaviours of Valve Seat Inserts Produced from High Chromium White Iron
  7. A Characterization for the Hot Flow Behaviors of As-extruded 7050 Aluminum Alloy
  8. A Characterization of Hot Flow Behaviors Involving Different Softening Mechanisms by ANN for As-Forged Ti-10V-2Fe-3Al Alloy
  9. Effect of Microwave Heating Conditions on the Preparation of High Surface Area Activated Carbon from Waste Bamboo
  10. Laboratory Study on Oxide Inclusions in High-Strength Low-Alloyed Steel Refined by Slag with Basicity 2–5
  11. Processing and Characterization of CrB2-Based Novel Composites
  12. Dispersion of Particles in the Emulsion by the Electric Current
  13. Description of Grain Refinement by Dynamic Recrystallization Under Hot Compressions for As-Extruded 3Cr20Ni10W2 Heat-Resistant Alloy
  14. Identification of Stable Processing Parameters in Ti–6Al–4V Alloy from a Wide Temperature Range Across β Transus and a Large Strain Rate Range
  15. Life Estimation and Creep Damage Quantification of Service Exposed Reformer Tube
Sign up now to receive a 20% welcome discount
Institutional Access
How does access work?
Have an idea on how to improve our website?
Please write us.
© 2025 De Gruyter Brill
Downloaded on 9.9.2025 from https://www.degruyterbrill.com/document/doi/10.1515/htmp-2014-0089/html
Scroll to top button