Preparing Soft Magnetic Composites for Structural and Micromechanical Investigations
-
T. Schwark
Abstract
Soft Magnetic Composites (SMC) consist of pure iron particles with an inorganic phosphorous coating and an additional iron oxide layer at the boundaries between them. It should be specified if the iron oxide is at the boundary of iron and the phosphorous coating or at the outer layer. It is assumed that it's a layer between the iron and the phosphorous layer. This combination of “ductile” and “brittle” constituents represents a challenge for preparing a specimen suitable for both microstructural and micromechanical studies. In particular for micromechanical tests, such as microcompression, microcantilever beam bending, micro tensile tests, and nanoindentation, the quality of the surface is critical. We demonstrate the effect of different surface preparation methods both on the microstructure and the mechanical properties. Mechanical polishing with two different end-polishing steps and combinations of mechanical polishing and ion-beam polishing are compared. Electron microscopy clearly showed the damaged or deformed surface layer of SMC specimens polished only mechanically, which significantly affected the mechanical properties as determined by nanoindentation. The microstructure of the particles was examined with electron backscatter diffraction and transmission electron microscopy revealing a subgrain structure within the particles. While the boundaries do not exhibit any cracks after indentation, the hardness of the boundaries and the adjacent material is clearly enhanced.
Kurzfassung
Weichmagnetische Kompositwerkstoffe (Soft Magnetic Composites, SMC) bestehen aus reinen Eisenpartikeln mit einer anorganischen Phosphorbeschichtung und einer zusätzlichen Eisenoxidschicht in der Grenzfläche. Diese Kombination aus „duktilen“ und „spröden“ Bestandteilen stellt eine Herausforderung bei der Präparation einer Probe dar, die sowohl für mikrostrukturelle als auch für mikromechanische Untersuchungen geeignet ist. Gerade für mikromechanische Tests wie Mikrodruck-, Mikrobiege- und Mikrozugversuche und Nanoindentation ist die Qualität der Oberfläche entscheidend. Wir zeigen die Auswirkungen verschiedener Methoden zur Oberflächenpräparation sowohl auf die Mikrostruktur als auch die mechanischen Eigenschaften. Dabei werden mechanisches Polieren mit zwei unterschiedlichen Endpoliturschritten mit Kombinationen von mechanischem Polieren und Ionenstrahlpolieren miteinander verglichen. Elektronenmikroskopie zeigte deutlich die beschädigte oder deformierte Oberflächenschicht von SMC-Proben, die nur mechanisch poliert wurden. Diese wirkte sich gemäß durchgeführter Nanoindentationsmessungen erheblich auf die mechanischen Eigenschaften aus. Die Mikrostruktur der Partikel wurde mittels Elektronenrückstreubeugung und Transmissionselektronenmikroskopie untersucht, wobei eine Subkornstruktur innerhalb der Partikel zum Vorschein kam. Während die Grenzschichten nach der Indentierung keine Risse aufweisen, ist die Härte der Grenzschichten und des benachbarten Materials deutlich höher.
References / Literatur
[1] Oliver, W. C.; Pharr, G. M.: Journal of Materials Research, (1992) 7, 1564. 10.1557/JMR.1992.1564Suche in Google Scholar
[2] Pathak, S.; Michler, J.; Wasmer, K.; Kalidindi, S.: J Mater Sci, (2012) 47, 815. 10.1007/s10853-011-5859-zSuche in Google Scholar
[3] Lian, J.; Garay, J. E.; Wang, J.: Scripta Materialia, (2007) 56, 1095. 10.1016/j.scriptamat.2007.02.027Suche in Google Scholar
[4] Lucca, D. A.; Klopfstein, M. J.; Ghisleni, R.; Cantwell, G.: CIRP Annals – Manufacturing Technology, (2002) 51, 483.10.1016/S0007-8506(07)61566-2Suche in Google Scholar
[5] Shen, L.; Liu, T.; Lv, P.: Polymer Testing, (2005) 24, 746. 10.1016/j.polymertesting.2005.04.004Suche in Google Scholar
[6] Pathak, S.; Stojakovic, D.; Doherty, R.; Kalidindi, S. R.: Journal of Materials Research, (2009) 24, 1142. 10.1557/jmr.2009.0137Suche in Google Scholar
[7] Fischer-Cripps, A. C.: Nanoindentation, SpringerNew York: (2004). 10.1007/978-1-4757-5943-3Suche in Google Scholar
[8] Bureš, R. M. F.; Kollár, P.; Füzer, J.; Strečková, M.: Powder Metallurgy Progress, (2012) 12, 181.Suche in Google Scholar
[9] Giménez, S.; Lauwagie, T.; Roebben, G.; Heylen, W.; Van der Biest, O.: Journal of Alloys and Compounds, (2006) 419, 299. 10.1016/j.jallcom.2005.09.053Suche in Google Scholar
[10] Gilbert, I.; Bull, S.; Evans, T.; Jack, A.; Stephenson, D.; De Sa, A.: J Mater Sci, (2004) 39, 457. 10.1023/B:JMSC.0000011498.90378.7eSuche in Google Scholar
[11] Oikonomou, C.; Gutiérrez, D. C.; Monclús, M.; Molina-Adareguia, J. M.; Nyborg, L.: Assessment of the compacting and annealing process steps on the performance of finished Soft Magnetic Composite components, In T2 Euro PM2015 Proceedings, (2015).Suche in Google Scholar
[12] Marcin Karbowiak, B. J.; Kapelski, D.; Przybylski, M.; Slusarek, B.: Influence of grain size on mechanical properties of soft magnetic composites, In Euro PM2012 – PM Functional Materials, (2012); Vol. 1, pp 387.Suche in Google Scholar
[13] Yiping, D.; Youguang, G.; Jianguo, Z.: Investigation of motor topologies for SMC application, In Electrical Machines and Systems, 2007. ICEMS. International Conference on, (2007); pp 695.Suche in Google Scholar
[14] Svensson, L.; Frogner, K.; Jeppsson, P.; Cedell, T.; Andersson, M.: Journal of Magnetism and Magnetic Materials, (2012) 324, 2717. 10.1016/j.jmmm.2012.03.049Suche in Google Scholar
[15] Henaux, C.; Nogarede, B.; Harribey, D.: IEEE Transactions on Magnetics, (2012) 48, 2035. 10.1109/TMAG.2011.2181530Suche in Google Scholar
[16] Lin, Z. W.; Zhu, J. G.; Zhong, J. J.; Johansen, T. H.; Wang, X. L.; Yu, W. Y.: Journal of Applied Physics, (2007) 101, 09K107.10.1063/1.2713706Suche in Google Scholar
[17] Szabó, L.; Viorel, I.; Iancu, V.: Popa, D., Oradea University Annals, Electrotechnical Fascicle, (2004), 134.Suche in Google Scholar
[18] O. Andersson, P. H.: Advances in Soft Magnetic Composites – Materials and Applications, In PowderMet2009, Las Vegas, (2009); pp 1.Suche in Google Scholar
[19] Nguyen, H. G.; Hartmaier, G. D. A.: Grenze der Einsetzbarkeit eines weichmagnetischen Pulververbundwerkstoffes aus Sicht der Mechanik, In 19. Symposium Verbundwerkstoffe und Werkstoffverbunde, Karlsruhe, (2013).Suche in Google Scholar
[20] Kim, K.; Watanabe, M.; Kuroda, S.; Kawano, N.: Materials Transactions, JIM, (2011) 52, 439.10.2320/matertrans.T-M2010826Suche in Google Scholar
[21] N. Erdman, R. C., and Asahina, S.: Microscopy Today, (2006),Suche in Google Scholar
[22] Asahina, S.; F. C., Sam M.Stevens and Terasaki, O.: MC 2009, Instrumentation and Methodology, (2009) 1,Suche in Google Scholar
[23] Radi, Z.; Havancs, K.; x00E; Kal, S.; cska; Baris, A.: Surface polishing and slope cut by parallel ar ion beams for high resolution electron backscatter diffraction measurements, In 2014 International Conference on Nanoscience and Nanotechnology, (2014); pp 1. 10.1109/ICONN.2014.6965245Suche in Google Scholar
[24] Carter, G.; Nobes, M. J.; Katardjiev, I. V.: Vacuum, (1993) 44, 303. 10.1016/0042-207X(93)90174-9Suche in Google Scholar
[25] Mine, Y.; Hirashita, K.; Matsuda, M.; Otsu, M.; Takashima, K.: Corrosion Science, (2011) 53, 529. 10.1016/j.corsci.2010.10.019Suche in Google Scholar
[26] Mine, Y.; Hirashita, K.; Takashima, H.; Matsuda, M.; Takashima, K.: Materials Science and Engineering: A, (2013) 560, 535. 10.1016/j.msea.2012.09.099Suche in Google Scholar
[27] Mine, Y.; Takashima, H.; Matsuda, M.; Takashima, K.: Materials Science and Engineering: A, (2014) 618, 359. 10.1016/j.msea.2014.09.027Suche in Google Scholar
[28] Mine, Y.; Fujisaki, H.; Matsuda, M.; Takeyama, M.; Takashima, K.: Scripta Materialia, (2011) 65, 707. 10.1016/j.scriptamat.2011.07.012Suche in Google Scholar
[29] Levin, M. C.: Charakterisierung von weichmagnetischen Pulververbundwerkstoffen für den Einsatz in Traktionsantrieben, Verlag Dr. Hut: (2014).Suche in Google Scholar
[30] Pharr, G. M.; Herbert, E. G.; Gao, Y.: Annual Review of Materials Research, (2010) 40, 271. 10.1146/annurev-matsci-070909-104456Suche in Google Scholar
© 2017, Carl Hanser Verlag, München
Artikel in diesem Heft
- Contents/Inhalt
- Contents
- Editorial
- Editorial
- Technical Contributions/Fachbeiträge
- The Copper of the Kyffhäuser Monument
- Preparing Soft Magnetic Composites for Structural and Micromechanical Investigations
- Round Robin Test on the “Analysis of Graphite Shapes by Means of Microscopic Images of Cast Iron Samples” in the DGM Working Group “Quantitative Structural Analysis” of the Expert Committee Materialography
- Failure Analysis
- Cracks in Hot-Dip Galvanized Steel Components
- Meeting Diary/Veranstaltungskalender
- Meeting Diary
Artikel in diesem Heft
- Contents/Inhalt
- Contents
- Editorial
- Editorial
- Technical Contributions/Fachbeiträge
- The Copper of the Kyffhäuser Monument
- Preparing Soft Magnetic Composites for Structural and Micromechanical Investigations
- Round Robin Test on the “Analysis of Graphite Shapes by Means of Microscopic Images of Cast Iron Samples” in the DGM Working Group “Quantitative Structural Analysis” of the Expert Committee Materialography
- Failure Analysis
- Cracks in Hot-Dip Galvanized Steel Components
- Meeting Diary/Veranstaltungskalender
- Meeting Diary