Correlation Between the Microstructure of Galvannealed Coatings and the Defoliation during Press Forming
-
Moon-Hi Hong
Abstract
The defoliation properties of galvannealed coating, so-called powdering and flaking, in continuous galvanizing line were investigated by scanning electron microscopy, X-ray diffraction, roughness profiler and deep drawing test. Both aluminum content in molten zinc and galvannealing temperature were turned out to be critical factors on the microstructure and mechanical properties of galvannealed coatings. Below 0.135 wt% Al, coating surface composed of the mixture of granular d1p and columnar z phases. While, above 0.155 wt% Al, coating surface contained the mixture of granular d1p and pan-cake d1k phases. The appearance of brittle d1k phase approximately 10 μm in size can account for the high amount of defoliation during deep drawing test. The formation of relatively ductile z phase and thin G phase contributes to improve the press formability. The optimazation of the surface microstructure controlling the ratio of granular d1p and columnar z phases was important to reduce the powdering.
Kurzfassung
Das Abblätterverhalten von wärmebehandelten (GA) Zinkeschichtungen, das sogenannte Pulverisieren und Abschuppen, in Endlosverzinkungslinien wurde mittels Rasterelektronenmikroskopie, Röntgendiffraktion, Rauigkeitsmessungen und Tiefziehtests untersucht. Sowohl der Aluminiumgehalt in geschmolzenem Zink als auch die Wärmebehandlungstemperaur nach dem Verzinken (GA-Temperatur) erwiesen sich als kritische Faktoren für Gefüge und mechanische Eigenschaften der Zinkschichten. Unterhalb eines Gehalts von 0,135 Gew.-% Al setzte sich die Beschichtungsoberfläche aus einer Mischung von granularem d1p und stengeligen z-Phasen zusammen, während bei einem Gehalt von über 0,155 Gew.-% Al die Beschichtungsoberfläche aus einer Mischung von granularem d1p und flachen Scheiben aus d1k-Phasen bestand. Das Auftreten einer spröden d1k-Phase mit einer Größe von etwa 10 μm kann die große Menge des Abblätterns während des Tiefziehtests erklären. Die Bildung einer relativ duktilen z-Phase und einer dünnen G-Phase trägt zur Verbesserung der Druckverformbarkeit bei. Die Optimierung des Oberflächengefüges durch Steuerung des Verhältnisses von granularem d1p und stengeligen z-Phasen erwies sich als wichtig für die Reduzierung des Abblätterns.
Literatur/References
[1] Sakiyama, T.; Ichigawa, M.; Saito, Z.; Matsuzaki, Y.: CAMP-ISIJ, 3 (1990), 1508Suche in Google Scholar
[2] Guth, J.; Mataigne, J. M.: Proc. of GALVATECH’ 1995, Iron and Steel Society (Ed.), 17–21 September, Chicago, USA, 709–716Suche in Google Scholar
[3] Hong, M. H.; Saka, H.: Scripta Materialia., 36 (1997), 142310.1016/S1359-6462(97)00030-4Suche in Google Scholar
[4] Kato, T.; Hong, M. H.; Nunome, K.; Sasaki, K.; Kuroda, K.; Saka, H.: Thin Solid Film, 319 (1998), 13210.1016/S0040-6090(97)01108-5Suche in Google Scholar
[5] Saka, H.; Kato, T.; Hong, M. H.: J. of Surface Finishing Soc. of Japan, 51 (2000), 56810.4139/sfj.51.568Suche in Google Scholar
[6] Hong, M. H.; Saka, H.: Phil. Mag., A74 (1996), 50910.1080/01418619608242158Suche in Google Scholar
[7] Hong, M. H.; Saka, H.: Acta Materialia, 45 (1997), 422510.1016/S1359-6454(97)00079-7Suche in Google Scholar
[8] Okamoto, A.: Recent Progress and Future Prospects in Steel Sheets and Surface Treated Steel Sheets, 31, ISIJ (Ed.), Tokyo, Japan, 1998Suche in Google Scholar
[9] Marder, A. R.: Prog. in Mat. Sci., 45 (2000), 191–27110.1016/S0079-6425(98)00006-1Suche in Google Scholar
[10] Dauby, B.; Vankeleffe, P.; Feron, S.: Proc. of GALVATECH’ 1995, Iron and Steel Society (Ed.), 17–21 September, Chicago, USA, 717–722Suche in Google Scholar
[11] Mcdevitt, E.; Morimoto, Y.; Meshii, M.: ISIJ international, 37, (1997) 77610.2355/isijinternational.37.776Suche in Google Scholar
[12] Morimoto, Y.; Mcdevitt, E.; Meshii, M.: ISIJ international, 37 (1997), 90610.2355/isijinternational.37.906Suche in Google Scholar
[13] G. J.Harvey and P. D.Mercer: Metall. Trans., 4, (1973) 61910.1007/BF02648719Suche in Google Scholar
[14] Lin, C. S.; Meshii, M.: Met. & Mat. Trans. B, 25B (1994), 72110.1007/BF02655180Suche in Google Scholar
[15] Dubois, D.; Proc. of GALVATECH’ 2001, M.Lamberights (ed.), 26–28 June, Brussels, Belgium, 453Suche in Google Scholar
[16] Yamaguchi, S.; Makino, H.; Sakatoku, A.; Iguchi, Y.: Proc. of GALVATECH’ 1995, Iron and Steel Society (Ed.), 17–21 September, Chicago, USA, 647–655Suche in Google Scholar
[17] Van der Heiden, A., Burghardt, A. J.C., Van Koesveld, W., Perlstein, E. B., Spangers, M. G. J.: The Physical Metallurgy of Zinc Coated Steel, TMS annual meeting, San Francisco, 1994, 251Suche in Google Scholar
[18] Arai, M., Nakamori, T., Adachi, Y., Utsugi, T., CAMP-ISIJ, 5 (1992), 1649Suche in Google Scholar
[19] Gomi, S.; Kato, C.; Fujimura, T.; Mochizuki, K.: Zinc-Based Steel Coating Systems–Production and Performance, Goodwin, F. E. (Ed.), 16–19 February, 1998, San Antonio, USA, 147–156Suche in Google Scholar
© 2005, Carl Hanser Verlag, München
Artikel in diesem Heft
- Contents/Inhalt
- Inhalt / Contents
- Technical Contributions/Fachbeiträge
- Einfluss der Lagenanzahl auf die Kerbschlagarbeit bei Lagen- bzw. Schweissdamast
- Correlation Between the Microstructure of Galvannealed Coatings and the Defoliation during Press Forming
- Schadensfall Schäden an Kupferrohren einer Fußbodenheizung
Artikel in diesem Heft
- Contents/Inhalt
- Inhalt / Contents
- Technical Contributions/Fachbeiträge
- Einfluss der Lagenanzahl auf die Kerbschlagarbeit bei Lagen- bzw. Schweissdamast
- Correlation Between the Microstructure of Galvannealed Coatings and the Defoliation during Press Forming
- Schadensfall Schäden an Kupferrohren einer Fußbodenheizung